WO2025251702 - DEEP EMBOSSING-TOLERABLE PRIMER-TOPCOAT SYNCRETIC COATING FOR HOME APPLIANCE PANELS, AND PREPARATION METHOD THEREFOR
National phase entry is expected:
Publication Number
WO/2025/251702
Publication Date
11.12.2025
International Application No.
PCT/CN2025/080143
International Filing Date
03.03.2025
Title **
[English]
DEEP EMBOSSING-TOLERABLE PRIMER-TOPCOAT SYNCRETIC COATING FOR HOME APPLIANCE PANELS, AND PREPARATION METHOD THEREFOR
[French]
REVÊTEMENT SYNCRÉTIQUE DE PRIMAIRE-COUCHE DE FINITION TOLÉRABLE AU GAUFRAGE PROFOND POUR PANNEAUX D'APPAREIL MÉNAGER, ET PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT
[Chinese]
一种耐深压花家电板用底面合一面漆及其制备方法
Applicants **
CNOOC CHANGZHOU PAINT AND COATINGS INDUSTRY RESEARCH INSTITUTE CO., LTD
CNOOC CHANGZHOU ENVIRONMENTAL PROTECTION COATING CO., LTD
Inventors
FENG, Chunmiao
LI, Yang
ZHOU, Chunli
WU, Kuilu
HU, Yang
Priority Data
202410705247.7
03.06.2024
CN
Application details
| Total Number of Claims/PCT | * |
| Number of Independent Claims | * |
| Number of Priorities | * |
| Number of Multi-Dependent Claims | * |
| Number of Drawings | * |
| Pages for Publication | * |
| Number of Pages with Drawings | * |
| Pages of Specification | * |
| * | |
| Number of Office Actions | * |
| * | |
International Searching Authority |
CNIPA
* |
| Recordal of a Change of the Applicant's Name/Address |
Change of Applicant's Name and Address
* |
| Type of Assignment |
The Standard Agent's Assignment
* |
| Applicant's Legal Status |
Legal Entity
* |
| * | |
| * | |
| * | |
| * | |
| * | |
| Entry into National Phase under |
Chapter I
* |
| Patent Delivery |
Send the Letters Patent by Courier
* |
| Translation |
|
* The data is based on automatic recognition. Please verify and amend if necessary.
** IP-Coster compiles data from publicly available sources. If this data includes your personal information, you can contact us to request its removal.
Quotation for National Phase entry
| Country | Stages | Total | |
|---|---|---|---|
| China | Filing, Examination, Granting | 1577 | |
| EPO | Filing, Examination, Granting | 11551 | |
| Japan | Filing, Examination, Granting | 2000 | |
| South Korea | Filing, Examination, Granting | 1802 | |
| USA | Filing, Examination, Granting | 4740 |
Total:
21,670
Contact Us
Abstract[English]
Disclosed in the present invention are a deep embossing-tolerable primer-topcoat syncretic coating for home appliance panels, and a preparation method therefor. The primer-topcoat syncretic coating comprises the following components by weight: 20-35 parts of a modified polyester resin, 3-10 parts of a polyester resin having a high molecular weight, 6-10 parts of a curing agent, 20-35 parts of a pigment and filler, 0.4-1 part of wax powder, 2-3 parts of an auxiliary agent and 15-30 parts of a mixed solvent, wherein the modified polyester resin is a polyester polyurethane resin, and is prepared by means of an addition polymerization reaction of a polyester polyol resin and a diisocyanate compound. A single coating layer formed by said primer-topcoat syncretic coating exhibits excellent adhesion, machinability, corrosion resistance, and adaptability to different types of base materials, and especially has good tolerance to deep embossing, thereby possessing a broad application prospect in the market of colored coated panels.[French]
La présente invention divulgue un revêtement syncrétique de primaire-couche de finition tolérable au gaufrage profond pour des panneaux d'appareil ménager, et un procédé de préparation s'y rapportant. Le revêtement syncrétique de primaire-couche de finition comprend les composants suivants en poids : de 20 à 35 parties d'une résine de polyester modifiée, de 3 à 10 parties d'une résine de polyester ayant un poids moléculaire élevé, de 6 à 10 parties d'un agent de durcissement, de 20 à 35 parties d'un pigment et d'une charge, de 0,4 à 1 partie de poudre de cire, de 2 à 3 parties d'un agent auxiliaire et de 15 à 30 parties d'un solvant mixte, la résine de polyester modifiée étant une résine de polyuréthane de polyester, et étant préparée au moyen d'une réaction de polymérisation par addition d'une résine de polyol de polyester et d'un composé diisocyanate. Une couche unique de revêtement formée par ledit revêtement syncrétique de primaire-couche de finition présente une excellente adhérence, une excellente usinabilité, une excellente résistance à la corrosion et une excellente adaptabilité à différents types de matériaux de base, et présente en particulier une bonne tolérance au gaufrage profond, possédant ainsi une large perspective d'application sur le marché des panneaux revêtus colorés.[Chinese]
本发明公开了一种耐深压花家电板用底面合一面漆及其制备方法。所述底面合一面漆包括以下重量份的组分：改性聚酯树脂20-35份、高分子量聚酯树脂3-10份、固化剂6-10份、颜填料20-35份、蜡粉0.4-1份、助剂2-3份、混合溶剂15-30份。所述改性聚酯树脂为聚酯聚氨酯树脂，是通过聚酯多元醇树脂和二异氰酸酯化合物加成聚合反应制得。本发明制备的家电板用底面合一面漆形成的单一涂层具有优异的附着力、机械加工性、耐腐蚀性和对不同类型底材的适应性，尤其是具备良好的耐深压花性能，在彩涂板市场应用前景广阔。